R. Oberti | Search USGS

USGS1996

Lithium-bearing fluor-arfvedsonite from Hurricane Mountain, New Hampshire: A crystal-chemical study

The structures of two crystals of Li-bearing fluor-arfvedsonite (1) (K0.32Na0.68)Na2(Li0.48Fe 2+2.83Mn2+0.10Zn 0.06Fe3+1.46Ti0.07) (Si7.88Al0.12)O22[Fu1.15(OH) 0.85] and (2) (K0.25Na0.75)Na2(Li0.48Fe 2+2.84Mn2+0.11Zn 0.05Fe3+1.45Ti0.07)(Si 7.89Al0.11)O22[F1.35(OH) 0.65] from a granitic pegmatite, Hurricane Mountain, New Hampshire, have been refined to R indices of 1.5(1.6)% based on 1380(1387) reflections measured with MoK?? X-radiation. The unit cell parameters are (1) a 9.838(4), b 17.991(6), c 5.315(2) A??, 103.78(3)??, V 913.7 A??3 and (2) a 9.832(3), b 17.990(7), c 5.316(3) A??, ?? 103.79(3)??, V 913.2 A??3. Site-scattering refinement shows Li to be completely ordered at the M(3) site in these crystals. The amphibole composition is intermediate between fluor-arfvedsonite and fluor-ferro-leakeite with a small component (???10%) of fluor-ferro-ferri-nybo??ite. These amphibole crystals project into miarolitic cavities in a pegmatitic phase of a riebeckite granite. The early-crystallizing amphibole is close to fluor-ferro-leakeite in composition, but becomes progressively depleted in Li and F as crystals project out into miarolitic cavities; the final amphibole to crystallize is a fibrous Li-poor riebeckite. Li plays a significant role in late-stage fractionation involving the crystallization of alkali amphibole in peralkaline granitic environments.

Canadian Mineralogist↗

USGS1996

Fluor-ferro-leakeite, NaNa2(FC2+2Fe3+2Li)Si8O22F2, a new alkali amphibole from the Canada Pinabete pluton, Questa, New Mexico, U.S.A.

Fluor-ferro-leakeite is a new amphibole species from the Canada Pinabete pluton, Questa, New Mexico, U.S.A.; it occurs in association with quartz, alkali feldspar, acmite, ilmenite, and zircon. It forms as anhedral bluish black crystals elongated along c and up to 1 mm long. It is brittle, H = 6, Dmeas = 3.37 g/cm3, Dcalc = 3.34 g/cm3. In plane-polarized light, it is strongly pleochroic, X = very dark indigo blue, Y = gray blue, Z = yellow green; X ??? c = 10?? (in ??obtuse), Y = b, Z ??? a = 4?? (in ?? obtuse), with absorption X > Y > Z. Fluor-ferro-leakeite is biaxial positive, ?? = 1.675(2), ??= 1.683(2), ?? = 1.694(1); 2V = 87(2)??; dispersion is not visible because of the strong absorption. Fluor-ferro-leakeite is monoclinic, space group C2/m, a = 9.792(1), b = 17.938(1), c = 5.3133(4) A??, ??= 103.87(7)??, V = 906.0(1) A??3, Z = 2. The ten strongest X-ray diffraction lines in the powder pattern are [d(I,hkl)]: 2.710(100,151), 2.536(92,202), 3.404(57,131), 4.481(54,040), 8.426(45,110), 2.985(38,241), 2.585(38,061), 3.122(29,310), 2.165(26,261), and 1.586(25,403). Analysis by a combination of electron microprobe, ion microprobe, and crystal-structure refinement (Hawthorne et al. 1993) gives SiO2 51.12, Al2O3 1.13, TiO2 0.68, Fe2O3 16.73, FeO 8.87, MgO 2.02, MnO 4.51, ZnO 0.57, CaO 0.15, Na2O 9.22, K2O 1.19, Li2O 0.99, F 2.87, H2Ocalc 0.60, sum 99.44 wt%. The formula unit, calculated on the basis of 23 O atoms, is (K0.23Na0.76)(Na1.97Ca0.03)(Mg 0.46Fe2+1.4Mn2+0.59Zn0.07Fe3+1.93-Ti 0.08Al0.02Li0.61])(Si7.81Al 0.19)O22(F1.39OH0.61). A previous crystal-structure refinement (Hawthorne et al. 1993) shows Li to be completely ordered at the M3 site. Fluor-ferro-leakeite, ideally NaNa2(Fe2+2Fe3+2Li)Si8O22F2, is related to leakeite, NaNa2(Mg2Fe3+3Li)Si 8O22(OH)2, by the substitutions Fe2+ ??? Mg and F ??? OH.

American Mineralogist↗